Birla Carbon
N220 carbon black supplier China
Shandong Birla Carbon publishes N220. The colloidal properties below are the published typicals in Birla Carbon's rubber products guide, in the table titled Typical Colloidal Properties (ASTM D1765). Each of those figures is rated. Tint strength is included.
Specifications
| N220 NSA, published typicalASTM D6556 | 114 m²/g |
|---|---|
| N220 OAN, published typicalASTM D2414 | 114 ml/100g |
| N220 STSA, published typicalASTM D6556 | 106 m2/g |
| N220 tint strength, published typicalASTM D3265 | 116 % |
| N220 iodine number, published typicalASTM D1510 | 121 mg/g |
| N220 COAN, published typicalASTM D3493 | 98 ml/100g |
| N220 pour density, published typicalASTM D1513 | 355 kg/m3 |
| Furnace black particle size, from the rubber products guide | Typical carbon black particle sizes for furnace blacks range from approximately 8 nanometers to 100 nanometers. |
| CAS number, from the rubber products guide | 1333-86-4 |
| Jining location on the China carbon black SDS | Jining, Shandong Province, China |
| N220 listed on the China carbon black SDS | N220 |
| N220 on the Birla Carbon belts page | A standard, high surface area, medium structure reinforcing carbon black for lower hysteresis and durability in conveyor belts, tracks and general purpose masterbatch and compounding. |
| N220 on Birla Carbon's Spanish tread-grades page | A medium-structure, medium-surface-area grade for tread applications, mainly truck tread compounds where lower hysteresis is needed together with good tear, cut, and chip properties. An excellent general-purpose grade. |
The company location cited here is the city line the China carbon black SDS prints for Birla Carbon China (Jining) Co. Ltd.: Jining, Shandong Province, China.
The same SDS names N220 among the grades the SDS is valid for.
Birla Carbon's belts page names N220 and describes it as a standard, high surface area, medium structure reinforcing carbon black for lower hysteresis and durability in conveyor belts, tracks and general purpose masterbatch and compounding. Birla Carbon's Spanish tread-grades page names N220 for tread. The English rendering of that sentence is in the table.
Request a quote
Data sources
Rubber products guide: https://www.birlacarbon.com/wp-content/uploads/2022/02/birla-carbon-brochure-rubber-products-guide.pdf China carbon black SDS: https://www.birlacarbon.com/wp-content/uploads/hse/CHINA-GHS-RCB-ENGLISH.pdf
Cited values
- What is the cited value for N220 NSA, published typical?
- 114 m²/gASTM D6556
- What is the cited value for N220 STSA, published typical?
- 106 m2/gASTM D6556
- What is the cited value for N220 tint strength, published typical?
- 116 %ASTM D3265
- What is the cited value for N220 iodine number, published typical?
- 121 mg/gASTM D1510
- What is the cited value for N220 OAN, published typical?
- 114 ml/100gASTM D2414
- What is the cited value for N220 COAN, published typical?
- 98 ml/100gASTM D3493
- What is the cited value for N220 pour density, published typical?
- 355 kg/m3ASTM D1513
- What is the cited value for Furnace black particle size, from the rubber products guide?
- Typical carbon black particle sizes for furnace blacks range from approximately 8 nanometers to 100 nanometers.
- What is the cited value for CAS number, from the rubber products guide?
- 1333-86-4
- What is the cited value for Jining location on the China carbon black SDS?
- Jining, Shandong Province, China
- What is the cited value for N220 listed on the China carbon black SDS?
- N220
- What is the cited value for N220 on the Birla Carbon belts page?
- A standard, high surface area, medium structure reinforcing carbon black for lower hysteresis and durability in conveyor belts, tracks and general purpose masterbatch and compounding.
- What is the cited value for N220 on Birla Carbon's Spanish tread-grades page?
- A medium-structure, medium-surface-area grade for tread applications, mainly truck tread compounds where lower hysteresis is needed together with good tear, cut, and chip properties. An excellent general-purpose grade.
Last updated 2026-10-15